1 Risø National Laboratory for Sustainable Energy, Technical University of Denmark2 Department of Mechanical Engineering, Technical University of Denmark
Contradictory results have been concluded from transmission electron microscopy studies of disorientations evolving during plastic deformation: whereas saturation of the average disorientation angles across all dislocation boundaries was reported, a continued increase was observed, if different boundary types were distinguished. The apparent saturation is traced to a nontrivial artifact of the evaluation procedure. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Scripta Materialia, 2005, Vol 53, Issue 6, p. 757-762