1 Department of Civil Engineering, Technical University of Denmark2 Section for Construction Materials, Department of Civil Engineering, Technical University of Denmark
Cement stabilized gravel is an attractive material in road construction because its strength prop-erties are accommodating the increasingly higher requirements to the bearing capacity of a base course. However, reflection cracking of cement stabilized gravel is a major concern. In this pa-per the shrinkage properties of cement stabilized gravel have been documented under various temperature and relative humidity conditions. Two cement contents corresponding to a 28-days compressive strength of 6.2 MPa and 12.3 MPa have been tested and compared. It is found that the coefficient of linear expansion for the two cement contents is 9.9 × 10-6 ⁰C-1 and 11.3 × 10-6 ⁰C-1, respectively. Furthermore, it is found that reflecting cracking can mainly be explained by temperature dependent shrinkage rather than moisture dependent shrinkage.
Proceedings of the Xxii Nordic Concrete Research Symposium, 2014
Cement stabilized gravel; Reflection cracking; Temperature dependent shrinkage; Coefficient of linear expansion; Moisture dependent shrinkage