Fernandez, Santiago Martin1; Li, Qingfeng1; Steenberg, Thomas3; Jensen, Jens Oluf1
1 Department of Energy Conversion and Storage, Technical University of Denmark2 Proton conductors, Department of Energy Conversion and Storage, Technical University of Denmark3 Danish Power Systems ApS
A new electrode concept was proved with no polymeric binder in the catalyst layer for acid-doped polybenzimidazole (PBI) membrane fuel cells. It shows that a stable interface between the membrane and the catalyst layer can be retained when a proton conducting acid phase is established. The absence of the polymer in the catalytic layer turned out to be beneficial for the PBI cell performance particularly under high load operation. The influence on performance of the Pt loading of the cathode was studied in a range from 0.11 to 2.04 mgPt cm−2 showing saturation of the maximum performance for Pt loadings higher than 0.5 mgPt cm−2. For fuel cell operation on H2 and air supplied under ambient pressure, a peak power density as high as 471 mW cm−2 was measured. The tolerance to carbon monoxide (CO) was also studied with Pt loadings of the anode ranging from 0.24 to 1.82 mgPt cm−2. Lifetime test for a MEA loaded with 0.96 mgPt cm−2 on both electrodes revealed no voltage decay during 900 h of uninterrupted operation at 200 mA cm−2 and 160 °C.
Journal of Power Sources, 2014, Vol 272, p. 559-566
Gas diffusion electrode; High temperature PEMFC; PBI; Binder; CO poisoning; Durability