Magnetron sputtered coatings of aluminium containing up to 18 wt.% titanium were deposited on aluminium substrates to study the effect of microstructure on the optical appearance of the anodised layer. The microstructure and morphology were studied using transmission electron microscopy (TEM), X-ray diffraction (XRD), and glow discharge optical emission spectroscopy (GDOES), while the optical appearance was investigated using photospectrometry. The microstructure of the coatings was varied by heat treatment, resulting in the precipitation of Al3Ti phases. The reflectance of the anodised surfaces decreasedwith titaniumcontent in the as-deposited, and heat-treated states, and after anodisation of the as-deposited coatings. Specimens turned grey or blackwhen anodising after heat treatment. Partially anodised Al3Ti phaseswere found in the anodised layer, and the interface between substrate and anodised layer was rough, causing light trapping. Progressive darkening of the anodised layer is assumed to be due to the synergetic effect of morphology of incorporated intermetallics and substrate interface.
Surface and Coatings Technology, 2014, Vol 254
Aluminium; Titanium; Anodisation; Microstructure; Appearance; TEM