1 Risø National Laboratory for Sustainable Energy, Technical University of Denmark2 unknown
A number of specimens of CuCrZr alloy was prime aged and then overaged at 600oC for 1, 2 and 4 hours and for 4 hours at 700 and 850oC. After different heat treatments, both the precipitate microstructure and mechanical properties were characterized.Mechanical properties were determined at 50 and 300oC. Some selected specimens in the prime aged as well as overaged conditions were irradiated in the BR-2 reactor at Mol at 60 and 300oC to a displacement dose level of ~0.3 dpa. Irradiated specimens weremechanically tested at 60 and 300oC. The post-deformation microstructure of the irradiated specimens was examined in the transmission electron microscope. Results of the present investigations are presented in section 3. A brief summary of the mainresults and conclusions is given in section 4.